[CCMC 13562-R] CCMC Canadian code compliance evaluation

From: National Research Council Canada

CCMC number:

13562-R

Status:

Active

Issue date:

2012-09-20

Modified date:

2022-12-02

Evaluation holder:

Soprema Inc.

1688, rue Jean-Berchmans-Michaud
Drummondville QC J2C 8E9
Canada
Website: www.soprema.ca
Telephone: 819-478-2400, 866-478-2400
Email: info@soprema.ca

Product name:

Elastophene 1500, Resisto Self-Adhered Waterproofing Membrane, Membrane d’Étanchéité autocollante de Resisto

Code compliance:

NBC 2010, OBC

Evaluation requirements:

CCMC-TG-071326.01-10 "CCMC Technical Guide for Self-Adhered Modified Bituminous Membrane for Waterproofing Concrete Foundation Walls"

In most jurisdictions this document is sufficient evidence for approval by Canadian authorities.

Learn more about CCMC recognition Look for the trusted CCMC mark on products to verify compliance.

Code compliance opinion

It is the opinion of the Canadian Construction Materials Centre that the evaluated product, when used as a self-adhered, modified bituminous membrane for waterproofing below-ground concrete foundation walls in accordance with the conditions and limitations stated in this evaluation, complies with the following code:

National Building Code of Canada 2010

ID	Code provision	Solution type
09-13-03-01-01-b-00	9.13.3.1.(1)(b) Required Waterproofing	Acceptable
09-13-03-02-00-0-00	9.13.3.2.(1) Except as otherwise specified in this Se ...	Alternative
09-13-03-03-00-0-00	9.13.3.3.(1) The method of application of all bitumin ...	Alternative
09-13-03-05-00-0-00	9.13.3.5.(1) Concrete or unit masonry walls that are ...	Alternative

Ontario Building Code

Ruling No. 12-20-290 (13562-R) authorizing the use of this product in Ontario, subject to the terms and conditions contained in the Ruling, was made by the Minister of Municipal Affairs and Housing on 2012-12-20 pursuant to s.29 of the Building Code Act, 1992 (see Ruling for terms and conditions). This Ruling is subject to periodic revisions and updates.

The above opinion is based on the evaluation by the CCMC of technical evidence provided by the evaluation holder, and is bound by the stated conditions and limitations. For the benefit of the user, a summary of the technical information that forms the basis of this evaluation has been included.

Product information

Product name

Elastophene 1500, Resisto Self-Adhered Waterproofing Membrane, Membrane d’Étanchéité autocollante de Resisto

Product description

The product is a self-adhered, modified bituminous membrane intended to be used for waterproofing below-grade concrete foundation walls (poured-in-place and unit masonry walls). The membrane consists of a styrene-butadiene-styrene (SBS) modified bitumen that is laminated to a tri-laminated woven polyethylene film. A silicone release film is applied on the other side of the membrane to facilitate the installation. The membrane has vertical overlap markings to help installers achieve suitable overlaps at the seams.

The membrane is installed following the application of the manufacturer’s specified primer over the foundation wall and at the membrane seams. The membrane must be adequately adhered to the wall and to itself at the seams to prevent water infiltration in between the membrane and the wall and at the seams.

The membrane is available in two grades that are made of different modified bituminous blends. The grade is identified on the membrane: the regular grade for the summer (E/S) and the cold-weather grade for the winter (H/W).

The Elastophene1500 summer grade membrane is manufactured in rolls that measure 10 m × 1 m, 20 m × 1 m and 7 m × 0.5 m. The winter grade measures 20 m x 1 m. The Resisto Self-Adhered Waterproofing Membrane summer grade membrane is manufactured in rolls that measure 10 m × 1 m, 18.6 m × 1 m and 7 m × 0.5 m. The winter grade measures 18.6 m x 1 m. In both grades, the membrane is 1.5 mm thick.

Manufacturing plant

This evaluation is valid only for products produced at the following plant:

Product name	Manufacturing plant
Product name	Drummondville, QC, CA
Elastophene 1500, Resisto Self-Adhered Waterproofing Membrane, Membrane d’Étanchéité autocollante de Resisto	Product evaluated by the CCMC

Product evaluated by the CCMC Indicates that the product from this manufacturing facility has been evaluated by the CCMC

Conditions and limitations

The CCMC’s compliance opinion is bound by this product being used in accordance with the conditions and limitations set out below.

Use of the product has been evaluated for applications falling under the scope of Part 9 of Division B of the NBC 2010. The foundation walls must meet the structural requirements of the NBC 2010.
The poured-in-place concrete must be cured prior to the application of the product.
The maximum hydrostatic pressure the membrane and seams can sustain is 48 kPa.
Unit masonry or poured-in-place concrete walls must meet the surface preparation requirements of Article 9.13.3.4., Preparation of Surface, of Division B of the NBC 2010.
The concrete wall must be cleaned, dried and primed with exterior primer as per the manufacturer’s installation instructions prior to the installation of the membrane.
The product must be installed as per the manufacturer’s specified application temperature for the summer and winter grade.
The width of the overlap joint (seam) must be a minimum of 75 mm. The exterior primer must be applied along the overlap marking (75 mm) prior to the application of the next membrane.
The thickness of the membrane when installed on-site must be equivalent to the thickness of the evaluated product which is 1.5 mm.
The membrane rolls must be stored vertically on-site at a temperature less than the maximum temperature recommended by the manufacturer and must be protected from solar radiation as per the manufacturer’s instructions.
While the waterproofing continuity of the membrane to other parts of the wall (slabs, footing, etc.) is beyond the scope of this report, the installer must follow engineer-approved solutions to provide the waterproofing continuity.
A mastic must be applied to seal the top and bottom edges (terminations) of the membrane in accordance with the manufacturer’s instructions.
Following its application, the entire membrane must be protected from exposure to ultraviolet (UV) radiation from the sun within three weeks of its application and in accordance with the manufacturer’s additional recommendations.
The membrane must stop at grade level. Exposed above-grade portions of the membrane after soil settling must be protected from UV radiation and mechanical impact with additional backfill graded away from the foundation.
When used in soils containing high levels of organic matters, chemicals and microbiological activity, the manufacturer must be consulted to determine suitability.
Prior to backfilling, the membrane must be covered with a protection board that consists of a semi- or rigid board with a smooth surface facing the membrane (e.g., mineral fibre boards, EPS/XPS boards). The use of mechanically attached board systems may affect the waterproofing performance of the product. The manufacturer must provide instructions for the selection of appropriate fasteners and evidence that such fasteners produce a permanent waterproof seal for the foundation. If any self-seal performance is claimed by the manufacturer, then evidence must be supplied as to the extent of the capability and how tests were performed.
The foundation wall must be backfilled in accordance with the requirements of the Subsection 9.12.3., Backfill, of Division B of the NBC 2010.
The product must be applied in accordance with the manufacturer’s installation instructions by qualified installers using the manufacturer’s recommended tools.
The product must be identified with the phrase “CCMC 13562-R.”

Technical information

This evaluation is based on demonstrated conformance with the following criteria:

Evaluation requirements
Criteria number	Criteria name
CCMC-TG-071326.01-10	CCMC Technical Guide for Self-Adhered Modified Bituminous Membrane for Waterproofing Concrete Foundation Walls

The evaluation holder has submitted technical documentation for the CCMC’s evaluation. Testing was conducted at laboratories recognized by the CCMC. The corresponding technical evidence for this product is summarized below

Material requirements

Table 1. Results of testing the material requirements of the product
Property	Unit	Requirement	Result
Property	Unit	Requirement	Summer grade		Winter grade
Thickness variation	%	±10% of the manufacturer’s declared value	0.01^{Table footnote (1)}	0.05^{Table footnote (1)}
Hardness (Type 00 hardness gauge)	−	Report value	82.1	81.4
Water vapour permeance (WVP), Procedure B	ng/(Pa∙s∙m²)	±10% of the manufacturer’s declared value	1.32	1.24
Tensile strength at break - machine direction	kN/m^{Table footnote (2)}	Report value	11.91	12.38
Tensile strength at break - cross-machine direction	kN/m^{Table footnote (2)}	Report value	13.57	13.67

Performance requirements

Table 2. Results of testing the watertightness performance of the product
Property^{Table footnote (1)}^, ^{Table footnote (2)}	Requirement	Result
Property^{Table footnote (1)}^, ^{Table footnote (2)}	Requirement	Summer grade	Winter grade
Watertightness	No leakage	Pass
Water immersion/watertightness	No leakage	Pass
Heat aging/watertightness	No leakage	Pass
Chemical aging (NaOH)/watertightness	No leakage	Pass
Chemical aging (acetic acid)/watertightness	No leakage	Pass
UV aging/watertightness	No leakage	Pass
Low temperature flexibility/watertightness	No leakage	Pass

Table 3. Results of testing the crack bridging resistance of the product
Property^{Table footnote (1)}		Requirement	Result
Property^{Table footnote (1)}		Requirement	Summergrade	Winter grade
Crack bridging	30 cycles at –20°C 30 cycles at 30°C	No cracking, breakage, tearing, adhesion failure or other observable failures	Pass
Water immersion/ crack bridging	30 cycles at −20°C 30 cycles at 30°C	No cracking, breakage, tearing, adhesion failure or other observable failures	Pass
Heat aging/crack bridging	10 cycles at −20°C 10 cycles at 30°C	No cracking, breakage, tearing, adhesion failure or other observable failures	Pass
Chemical aging (NaOH)/crack bridging	10 cycles at −20°C 10 cycles at 30°C	No cracking, breakage, tearing, adhesion failure or other observable failures	Pass
Chemical aging (acetic acid)/crack bridging	10 cycles at −20°C 10 cycles at 30°C	No cracking, breakage, tearing, adhesion failure or other observable failures	Pass
UV aging/crack bridging	10 cycles at −20°C 10 cycles at 30°C	No cracking, breakage, tearing, adhesion failure or other observable failures	Pass

Table 4. Results of testing the peel adhesion performance of the product
Property^{Table footnote (1)}	Unit^{Table footnote (2)}	Requirement	Result
Property^{Table footnote (1)}	Unit^{Table footnote (2)}	Requirement	Summer grade	Winter grade
Peel adhesion	N/m	≥ 175	1 239	1 120
Water immersion/peel adhesion	N/m	158 (≥ 90% of 175)	984	367
Heat aging/peel adhesion			949	526
UV aging/peel adhesion			2 581	592

Table 5. Results of testing the tensile strength of the product
Property^{Table footnote (1)}	Unit^{Table footnote (2)}	Requirement^{Table footnote (3)}	Result^{Table footnote (4)}
Property^{Table footnote (1)}	Unit^{Table footnote (2)}	Requirement^{Table footnote (3)}	Summer grade	Winter grade
Heat aging/tensile strength	kN/m	Summer grade ≥ 10.72 Winter grade ≥ 11.14 (≥ 90% of original value)	13.00	13.08
Chemical aging (NaOH)/tensile strength			12.85	12.28
Chemical aging (acetic acid)/tensile strength			12.12	11.93
UV aging/tensile strength			11.96	11.93

Table 6. Results of testing the performance properties of the lap joint on the product^{Table footnote (1)}
Property^{Table footnote (1)}	Requirement	Result
Property^{Table footnote (1)}	Requirement	Summer grade	Winter grade
Water immersion/watertightness^{Table footnote (2)}	No leakage	Pass
Heat aging/watertightness^{Table footnote (2)}	No leakage	Pass
Water immersion/peel adhesion	≥ 158 N/m (≥ 90% of 175)	1 280	982
Heat aging/peel adhesion		1 167	516
UV aging/peel adhesion		1 254	775
Lap joint shear test	No bounding and slippage failure prior to reaching the breaking strength of the membrane	Pass
Heat aging/lap joint shear test	No bounding and slippage failure prior to reaching the breaking strength of the membrane	Pass

Administrative information

Disclaimer

This evaluation is issued by the Canadian Construction Materials Centre (CCMC), a part of the Construction Research Centre at the National Research Council of Canada (NRC). The evaluation must be read in the context of the entire CCMC Registry of Product Assessments and the legislated applicable building code in effect.

The CCMC was established in 1988 on behalf of the applicable regulator (i.e., the provinces and territories) to ensure—through assessment—conformity of alternative and acceptable solutions to regional building codes as determined by the local authority having jurisdiction (AHJ) as part of the issuance of a building permit.

It is the responsibility of the local AHJs, design professionals, and specifiers to confirm that the evaluation is current and has not been withdrawn or superseded by a later issue. Please refer to the website or contact:

Canadian Construction Materials Centre
Construction Research Centre
National Research Council of Canada
1200 Montreal Road
Ottawa, Ontario, K1A 0R6
Telephone: 613-993-6189
Fax: 613-952-0268

The NRC has evaluated the material, product, system or service described herein only for those characteristics stated herein. The information and opinions in this evaluation are directed to those who have the appropriate degree of experience to use and apply its contents (i.e., AHJs, design professionals and specifiers). This evaluation is only valid when the product is installed in strict compliance with the stated conditions and limitations of evaluation and the applicable local building code. In circumstances where no applicable local building permit is issued and that no confirmation of compliance ‘for use in the intended field application’ is undertaken, this evaluation is null and void in all respects. This evaluation is provided without representation, warranty, or guarantee of any kind, expressed, or implied, and the NRC provides no endorsement for any evaluated material, product, system or service described herein. The NRC accepts no responsibility whatsoever arising in any way from any and all use and reliance on the information contained in this evaluation with respect to its compliance to the referenced code(s) and standard(s). The NRC is not undertaking to render professional or other services on behalf of any person or entity nor to perform any duty owed by any person or entity to another person or entity.

Language

Une version française de ce document est disponible.
In the case of any discrepancy between the English and French version of this document, the English version shall prevail.

Copyright

All rights reserved. No part of this publication may be reproduced, stored in a retrieval system, or transmitted in any form or by any means, electronic, mechanical, photocopying, recording or otherwise, without the prior written permission of the CCMC.

Code Compliance via Alternative Solutions

Where a design differs from the acceptable solutions in Division B, then it should be treated as an "alternative solution." A proponent of an alternative solution must demonstrate that the alternative solution addresses the same issues as the applicable acceptable solutions in Division B and their attributed objectives and functional statements. However, because the objectives and functional statements are entirely qualitative, demonstrating compliance with them in isolation is not possible. Therefore, Clause 1.2.1.1.(1)(b) identifies the principle that Division B establishes the quantitative performance targets that alternative solutions must meet. In many cases, these targets are not defined very precisely by the acceptable solutions [...] Nevertheless, Clause 1.2.1.1.(1)(b) makes it clear that an effort must be made to demonstrate that an alternative solution will perform as well as a design that would satisfy the applicable acceptable solutions in Division B—not “well enough” but “as well as.”

National Building Code of Canada, Sentence A-1.2.1.1.(1)(b)

The CCMC has determined that compliance with this provision of the Code has been demonstrated as an Alternative Solution. The evaluation report provides a summary of the basis of CCMC's compliance opinion.

CCMC's code compliance opinions

All CCMC evaluation reports are opinions of code compliance established in accordance with the National Building Code of Canada, Subsection 1.2.1. "Compliance with this Code," which requires compliance to be achieved by:

complying with the applicable acceptable solutions in Division B, or
using an alternative solution that will achieve at least the minimum level of performance required by Division B in the areas defined by the objective and functional statements attributed to the applicable acceptable solutions.

The CCMC assesses compliance with Canadian building, energy and safety codes, and is trusted by over 6,000 regulators across Canada.