[CCMC 13297-R] CCMC Canadian code compliance evaluation
From: National Research Council Canada

CCMC number: | 13297-R |
Status: | Active |
Issue date: | 2008-01-17 |
Modified date: | 2022-02-04 |
Evaluation holder: | Henry Company Canada
10, avenue Saint-Pierre |
Product name: | Blueskin® WP 200 |
Code compliance: | NBC 2005 |
Evaluation requirements: |
|
In most jurisdictions this document is sufficient evidence for approval by Canadian authorities.
Learn more about CCMC recognitionCode compliance opinion
It is the opinion of the Canadian Construction Materials Centre that the evaluated product, when used as a self-adhered modified bituminous membrane for waterproofing the exterior of concrete foundation walls in accordance with the conditions and limitations stated in this evaluation, complies with the following code:
National Building Code of Canada 2005
ID | Code provision | Solution type |
---|---|---|
09-13-03-01-01-b-00 | 9.13.3.1.(1)(b) Required Waterproofing | Alternative |
09-13-03-02-01-0-00 | 9.13.3.2.(1) Material Standards | Alternative |
09-13-03-03-01-0-00 | 9.13.3.3.(1) Standards for Application | Alternative |
09-13-03-05-01-0-00 | 9.13.3.5.(1) Application of Waterproofing Membranes | Alternative |
The above opinion is based on the evaluation by the CCMC of technical evidence provided by the evaluation holder, and is bound by the stated conditions and limitations. For the benefit of the user, a summary of the technical information that forms the basis of this evaluation has been included.
Product information
Product name
Blueskin® WP 200Product description
The Blueskin® WP 200 is a self-adhered modified bituminous membrane that consists of a styrene butadiene styrene (SBS) rubberized asphalt compound that is integrally laminated to a blue, high density polyethylene film.
Blueskin® WP 200 is manufactured in rolls that measure 20.3 m long, 0.9 m wide and 1.5 mm thick.
Manufacturing plant
This evaluation is valid only for products produced at the following plant:
Product name | Petrolia, Ontario, Canada |
---|---|
Blueskin® WP 200 | ⦿ |
⦿ Indicates that the product from this manufacturing facility has been evaluated by the CCMC
Conditions and limitations
The CCMC’s compliance opinion is bound by this product being used in accordance with the conditions and limitations set out below.
- The use of Blueskin® WP 200 has been evaluated for applications falling under the scope of Part 9 of Division B of the NBC 2005 for foundation walls at a depth up to 3.2 m. The foundation walls shall meet the structural requirements of the NBC 2005.
- Unit masonry or poured-in-place concrete walls shall meet the surface preparation requirements of the NBC 2005, Division B, Article 9.13.3.4.
- The poured-in-place concrete must be cured prior to the installation of Blueskin® WP 200.
- The wall and footing surface must be dried prior to the installation of Blueskin® WP 200.
- The wall shall be primed with Aquaprime™ and Aquatac™ as per the manufacturer’s instructions prior to the installation of the membrane.
- Blueskin® WP 200 must be applied in accordance with the manufacturer’s installation instructions by an informed and knowledgeable installer.
- The thickness of the membrane installed on site shall be of equal thickness to the evaluated membrane.
- The rolls of the membrane shall be stored on site vertically at a temperature not higher than the maximum temperature recommended by the manufacturer and shall be protected from solar radiation as per the manufacturer’s instructions.
- A mastic shall be applied to seal the top and bottom edges of the membrane in accordance with the manufacturer’s instructions.
- Following its installation, the membrane shall be protected to grade level from exposure to ultraviolet (UV) radiation within 48 hours of its application and in accordance with the manufacturer’s additional recommendations.
- Prior to backfilling, the membrane must be covered with a protection board meeting the manufacturer’s specifications. The use of mechanically attached board systems may affect the waterproofing performance of the product. The manufacturer shall provide instructions for the selection of adequate fasteners and proof that such fasteners produce a permanent waterproof seal for the foundation. If any self-seal performance is claimed by the manufacturer, then evidence must be supplied as to the extent of the capability and how tests were performed.
- The installers shall consult with the manufacturer to determine the appropriate permanent protection for the above-grade portion of the membrane from UV radiation and mechanical impact.
- The foundation wall must be backfilled in accordance with the requirements of the NBC 2005, Division B, Subsection 9.12.3.
- When used in soils containing high levels of organic matters, chemicals and microbiological activity, the manufacturer shall be consulted to determine suitability.
- Blueskin® WP 200 must be identified with the phrase “CCMC 13297-R.”
Technical information
This evaluation is based on demonstrated conformance with the following criteria:
Criteria number | Criteria name |
---|---|
CCMC-TG-071326.01-05 | CCMC Technical Guide for Bakor Inc. (Henry Company Canada) |
The evaluation holder has submitted technical documentation for the CCMC’s evaluation. Testing was conducted at laboratories recognized by the CCMC. The corresponding technical evidence for this product is summarized below.
See below the NBC 2005 compliance data for Blueskin® WP 200 on which the CCMC based its opinion in the code compliance opinion section.
Property | Unit | Requirement | Result |
---|---|---|---|
Thickness tolerance | % | ± 10 of the manufacturer’s specified value | –2.5 |
Hardness (type 00 hardness gauge) | No unit | Report value | 76 |
Water vapour permeance, procedure B | ng/(Pa·s·m2) | Report value | 0.7 |
Tensile strength at maximum load | MPa | Report value | 3.6 |
Elastic recovery | % | Report value | 44 |
PropertyTable footnote (1) | Unit | Requirement | Result |
---|---|---|---|
Watertightness | No unit | No leakage | Passed |
Water immersion/watertightness | No unit | No leakage | Passed |
Heat aging/watertightness | No unit | No leakage | Passed |
Chemical aging/watertightness | No unit | No leakage | Passed |
UV aging/watertightness | No unit | No leakage | Passed |
Low temperature flexibility/watertightness | No unit | No leakage | Passed |
PropertyTable footnote (1) | Unit | Requirement | Result | |
---|---|---|---|---|
Crack bridging | 30 cycles at –20°C | No unit | No cracking, breakage, tearing, adhesion failure or other observable failures | Passed |
30 cycles at 30°C | ||||
Water immersion/crack bridging | 30 cycles at –20°C | No unit | No cracking, breakage, tearing, adhesion failure or other observable failures | Passed |
30 cycles at 30°C | ||||
Heat aging/crack bridging | 10 cycles at –20°C | No unit | No cracking, breakage, tearing, adhesion failure or other observable failures | Passed |
10 cycles at 30°C | ||||
Chemical aging (NaOH)/crack bridging | 10 cycles at –20°C | No unit | No cracking, breakage, tearing, adhesion failure or other observable failures | Passed |
10 cycles at 30°C | ||||
Chemical aging (acetic acid)/crack bridging | 10 cycles at –20°C | No unit | No cracking, breakage, tearing, adhesion failure or other observable failures | Passed |
10 cycles at 30°C | ||||
UV aging/crack bridging | 10 cycles at –20°C | No unit | No cracking, breakage, tearing, adhesion failure or other observable failures | Passed |
10 cycles at 30°C |
PropertyTable footnote (1) | Unit | Requirement | Result |
---|---|---|---|
Water immersion/adhesion | N/m | > 175 | 1 427 N/m |
Heat aging/adhesion | N/m | > 175 | 1 118 N/m |
Heat aging/tensile strength | % | > 90% of original value | Table footnote (2) |
Chemical aging (NaOH)/tensile strength | % | > 90% of original value | Passed |
Chemical aging (acetic acid)/tensile strength | % | > 90% of original value | Passed |
UV aging/tensile strength | % | > 90% of original value | Table footnote (2) |
PropertyTable footnote (1) | Unit | Requirement | Result |
---|---|---|---|
Heat aging/elastic recovery | % | > 90% of original value | Passed |
Chemical aging (NaOH)/elastic recovery | % | > 90% of original value | Passed |
Chemical aging (acetic acid)/elastic recovery | % | > 90% of original value | Passed |
UV aging/elastic recovery | % | > 90% of original value | Passed |
PropertyTable footnote (1) | Unit | Requirement | Result |
---|---|---|---|
Water immersion/watertightness | No unit | No leakage | Passed |
Heat aging/watertightness | No unit | No leakage | Passed |
Water immersion/adhesion | N/m | > 175 | 1 449 N/m |
Heat aging/adhesion | N/m | > 175 | 582 N/m |
Lap joint shear test | No unit | No slippage or bounding failure | Passed |
Heat aging/lap joint shear test | No unit | No slippage or bounding failure | Passed |
Administrative information
Disclaimer
This evaluation is issued by the Canadian Construction Materials Centre (CCMC), a part of the Construction Research Centre at the National Research Council of Canada (NRC). The evaluation must be read in the context of the entire CCMC Registry of Product Assessments and the legislated applicable building code in effect.
The CCMC was established in 1988 on behalf of the applicable regulator (i.e., the provinces and territories) to ensure—through assessment—conformity of alternative and acceptable solutions to regional building codes as determined by the local authority having jurisdiction (AHJ) as part of the issuance of a building permit.
It is the responsibility of the local AHJs, design professionals, and specifiers to confirm that the evaluation is current and has not been withdrawn or superseded by a later issue. Please refer to the website or contact:
Canadian Construction Materials Centre
Construction Research Centre
National Research Council of Canada
1200 Montreal Road
Ottawa, Ontario, K1A 0R6
Telephone: 613-993-6189
Fax: 613-952-0268
The NRC has evaluated the material, product, system or service described herein only for those characteristics stated herein. The information and opinions in this evaluation are directed to those who have the appropriate degree of experience to use and apply its contents (i.e., AHJs, design professionals and specifiers). This evaluation is only valid when the product is installed in strict compliance with the stated conditions and limitations of evaluation and the applicable local building code. In circumstances where no applicable local building permit is issued and that no confirmation of compliance ‘for use in the intended field application’ is undertaken, this evaluation is null and void in all respects. This evaluation is provided without representation, warranty, or guarantee of any kind, expressed, or implied, and the NRC provides no endorsement for any evaluated material, product, system or service described herein. The NRC accepts no responsibility whatsoever arising in any way from any and all use and reliance on the information contained in this evaluation with respect to its compliance to the referenced code(s) and standard(s). The NRC is not undertaking to render professional or other services on behalf of any person or entity nor to perform any duty owed by any person or entity to another person or entity.
Language
Une version française de ce document est disponible.
In the case of any discrepancy between the English and French version of this document, the English version shall prevail.
Copyright
© 2022 Her Majesty the Queen in Right of Canada, as represented by the National Research Council of Canada.
All rights reserved. No part of this publication may be reproduced, stored in a retrieval system, or transmitted in any form or by any means, electronic, mechanical, photocopying, recording or otherwise, without the prior written permission of the CCMC.